Abstract
Approximately 25 cm × 25 cm large sheets of crosslinked highly porous poly(glycidyl methacrylate-co-ethyleneglycol dimethacrylate-co-ethylhexyl methacrylate) membranes with an average thicknesses between 285 and 565 μm were prepared by casting a high internal phase emulsion (HIPE) containing monomers onto glass substrates and subsequent polymerisation. Open cellular porous polyHIPE type membranes were obtained with large pores (cavity) sizes between 3 and 10 μm while interconnecting pores were between 1 and 3 μm. The percentage of ethylhexyl acrylate and ethyleneglycol dimethacrylate influenced the flexibility and morphology of the resulting membranes. Porous membranes were chemically modified with diethylamine to yield functionalised supports for ion exchange chromatography. Cylindrical housings were used for positioning of the membranes and allowing flow of the mobile phase. Pulse experiments were used to study the flow characteristics and a homogeneous flow through the entire area of the membrane was found. Bovine serum albumin was purified by a 8 ml column containing functional membrane in modular shape; dynamic binding capacity was measured to be as high as 45 mg/ml.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.