Embrittlement of Intercritically Reheated Coarse Grain Heat-Affected Zone of ASTM4130 Steel

Abstract

In this investigation, a thermal welding simulation technique was used to investigate the microstructures and mechanical properties of the intercritically reheated coarse grain heat-affected zone (IR CGHAZ) of ASTM4130 steel. The effect of post weld heat treatment (PWHT) on the toughness of IR CGHAZ was also analyzed. The toughness of IR CGHAZ was measured by means of Charpy impact, and it is found that IR CGHAZ has the lowest toughness which is much lower than that of the base metal regardless of whether PWHT is applied or not. The as-welded IR CGHAZ is mainly composed of ferrite, martensite, and many blocky M–A constituents distributing along grain boundaries and subgrain boundaries in a near-connected network. Also, the prior austenite grains are still as coarse as those in the coarse grain heat-affected zone (CGHAZ). The presence of the blocky M–A constituents and the coarsened austenite grains result in the toughness deterioration of the as-welded IR CGHAZ. Most of the blocky M–A constituents are decomposed to granular bainite due to the effect of the PWHT. However, PWHT cannot refine the prior austenite grains. Thus, the low toughness of IR CGHAZ after PWHT can be attributed to two factors, i.e., the coarsened austenite grains, and the presence of the remaining M–A constituents and granular bainite, which are located at grain boundaries and subgrain boundaries in a near-connected network. The absorbed energy of the IR CGHAZ was increased by about 3.75 times, which means that the PWHT can effectively improve the toughness but it cannot be recovered to the level of base metal.