Abstract
This study investigated the effects of electropulsing treatment (EPT) condition on the microstructure and microhardness of cold-rolled Grade 2 Ti sheet. Particular attention was paid to the dependence of the material properties on the electric current direction, referred to as electropulsing anisotropy. Direct-current (DC) EPT was applied along either the rolling direction (RD) or transverse direction (TD) of the rolled sheet. EPT along the TD resulted in a higher heating rate and maximum temperature, whereas that along the RD accelerated the static recrystallization (SRX) process under identical electropulsing parameters. Such a discrepancy was interpreted using the elongated grain structure and basal texture in the cold-rolled Ti sheet. These results were further supported by microhardness measurements, confirming the presence of electropulsing anisotropy during DC EPT in Ti alloys for the first time. In addition, the employed EPT was compared to a traditional furnace heat treatment (FHT) with rigorous temperature and time control, wherein the optimum EPT process spent only 13% of the processing time to complete SRX with a lower thermal energy requirement. This indicates a significant athermal contribution of EPT to electropulsing anisotropy.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.