Abstract
Porous polymeric near-spherical capsules, ~ 3.6 mm in diameter, were prepared using an electrodydrodynamic process. These capsules were pyrolysed to porous ceramics, ~ 3 mm in diameter. The ceramic capsules had interconnected pores of ~ 1.3 μm in size, and large cells with a mean size of 28 μm. The larger pores resemble the cells in a typical ceramic foam and were evenly distributed throughout the structure. A large proportion of the ceramic capsules contained 65–70% porosity, and their compressive strength was 0.2–0.4 MPa.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.