Abstract
The electrodeposition and surface morphology of aluminium on tungsten (W) and aluminium (Al) electrodes from 2 : 1 molar ratio AlCl 3–[EMIm]Cl ionic liquids were investigated. Analyses of the chronoamperograms indicate that the deposition process of aluminium on W substrates was controlled by instantaneous nucleation with diffusion-controlled growth, while the deposition processes of aluminium on Al electrodes were found to be associated with kinetic limitations. Constant potential deposition experiments showed that the electrodeposits obtained on both W and Al electrodes between − 0.10 and − 0.40 V (vs. Al(III)/Al) are dense, continuous and well adherent. Dense aluminium deposits were also obtained on Al substrates using constant current deposition between 10 and 70 mA/cm 2, and the current efficiency was found to be dependent of the current density varying from 85% to 100%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.