Abstract
In this paper, we investigate the challenges related to electrodeposition and characterization of magnetostrictive galfenol thin films as well as techniques used to overcome these issues. Successful deposition and evaluation of galfenol thin films is necessary for the design of galfenol based microelectromechanical devices. Stress is a primary concern because thick films and poor adhesion to substrates (e.g., silicon oxide) can lead to delamination and peeling. In addition, magnetostriction measurements require films that are uniform in thickness and composition over the sample area. Various adhesion layers were tested, and delamination was eliminated with Cr/Cu, which provided robust adhesion to the glass substrates used in capacitance bridge measurements. Uniformity and composition were controlled by the use of a rotating disk electrode for electrodeposition, which created a uniform boundary condition across the sample during deposition. The capacitance bridge technique was calibrated with Ni/glass samples, after which a magnetostriction of 140 ppm was measured for Fe83Ga17 films. These results represent the first magnetostriction measurements of electrodeposited galfenol.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.