Abstract
Electrochromic (EC) reaction of indium nitride (InN) films prepared by radio frequency (rf) ion plating was studied through their chemical bonding states and crystalline structures as measured by X‐ray photoelectron spectroscopy (XPS) and X‐ray diffraction (XRD), respectively. In addition, the pH dependence of the EC reaction was characterized. Color of the InN films became darker or lighter when the InN films were polarized anodically or cathodically, respectively, in a solution. Similar color changes were observed when pH of the solution was changed from 4.0 to 11.6. The color change at one unit of pH difference corresponded to the EC color change at a potential difference of 59 mV. From these results, and were confirmed to be active reactants in the EC reaction of the InN films. On the other hand, it was revealed from XPS and XRD results that the amount of hydroxides formed at the grain boundaries and the surface of the anodically polarized InN films was greater than that of the film polarized cathodically. Therefore, the electrochromism of the InN films was concluded to be governed by chemisorption of and at grain boundaries. © 1999 The Electrochemical Society. All rights reserved.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.