Abstract
WO3-x thin films were deposited on induim tin oxide (ITO) glass substrates with various oxygen flow ratios from 0.55 to 0.7 by the reactive facing-target sputtering method, at a power density of 4 W/cm2 and room temperature. The structural properties of the WO3-x thin films were measured by X-ray diffractometry and Raman spectral analysis. As-deposited WO3-x thin films had an amorphous structure. In the Raman spectra, WO3-x thin films exhibited two strong peaks at 770 and 950 cm-1 attributed to the vibrations of W6+–O and W6+=O bonds, respectively. The electrochemical and optical properties of WO3-x thin films were measured by cyclic voltammetry and UV/vis spectrometry. The results showed the highest charge density at an oxygen flow ratio of 0.7 and the highest transmittance in the visible range. The maximum coloration efficiency was 30.82 cm2/C at an oxygen flow ratio of 0.7.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.