Abstract
An X70 pipeline steel and a low-carbon steel with different types of coating defects were studied using corrosion tests in Ku’erle simulated soil solution containing 0.6000 mol/L Cl−. Electrochemical characteristics of the X70 pipeline steel with planar-defect epoxy-coating in simulated solutions of Ku’erle soil were tested. The results show that in 0.6000 mol/L Cl− simulated solution, for low-carbon steel with coating defects (the area ratio is 4.91%), at free corrosion potential and with immersion time, the corrosion with disbond was more severe than that with a break or with break and disbond. In Ku’erle soil simulated solution, when the coating defect area ratio was increased gradually (0.39% → 1.57% → 6.28%), the corrosion of the X70 steel under coating with break was promoted gradually, and the influence of immersion time on the corrosion decreased. The influence of the immersion time on the corrosion was weakened when the defect area ratio increased to a certain degree.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.