Abstract
Polyaniline (PANI) was synthesized by oxidative polymerization of aniline at different temperatures (5, 10, 15, 20 and 25 °C). The influence of polymerization temperature on sheet resistance of PANI was investigated, and the one prepared at 15 °C which showed lowest resistivity was chosen for further analysis. PANI was subsequently used as hole-injection layer (HIL) in polymer light emitting diodes (PLEDs) with structure of poly(ethylene terephthalate) (PET)/indium tin oxide (ITO)/PANI/MEH-PPV:BT/aluminum (Al). The PLEDs with emission layer made from a blend of poly [2-methoxy-5-(2′-ethyl-hexyloxy)-1,4-phenylene vinylene] (MEH-PPV) and an electron transporting material, benzothiadiazole (BT), were fabricated at room conditions without using glove boxes. Our results showed an improvement in performance of our PANI-based fabricated PLEDs (PET/ITO/PANI/MEH-PPV:BT/Al) compared to the conventional devices that use poly(3,4-ethylenedioxythiophene):polystyrene sulfonate (PET/ITO/PEDOT:PSS/MEH-PPV:BT/Al) as their HIL. The hole injection barrier height (φ) of the fabricated PLEDs were then estimated using the Fowler–Nordheim (FN) field-emission tunneling theory and revealed that the barrier height decreases by increasing the BT concentration in the MEH-PPV:BT blend layer.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.