Abstract
The piezoelectric properties of a solid solution of the binary system, x(Bi1/2Na1/2)TiO3–(1-x)(Bi1/2K1/2)TiO3 [BNKT100x; x=0.50–0.98] were investigated, focusing on depolarization temperature, Td. Fine piezoelectric properties in lead-free piezoelectric ceramics were obtained near the morphotropic phase boundary (MPB) composition between the rhombohedral and tetragonal structures, and the highest electromechanical coupling factor, k33, and piezoelectric constant, d33, were 0.56 for BNKT84 and 157 pC/N for BNKT80, respectively. However, the Td of BNKT80 was low (174 °C). The Td of the MPB composition was low, and the Td near the MPB composition was sharply decreased. It is thought that BNKT70 is a candidate composition for lead-free actuator applications owing to its relatively large piezoelectric constant, d33 (126 pC/N), dynamic d33 (214 pm/V), and high depolarization temperature, Td (206 °C). In this study, we determined depolarization temperature, Td, from the temperature dependence of dielectric and piezoelectric properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.