Abstract
Defect etching revealed a very large density (∼109cm−2) of intragrain defects in polycrystalline silicon (pc-Si) layers obtained through aluminum-induced crystallization of amorphous Si and epitaxy. Electron-beam-induced current measurements showed a strong recombination activity at these defects. Cathodoluminescence measurements showed the presence of two deep-level radiative transitions (0.85 and 0.93eV) with a relative intensity varying from grain to grain. These results indicate that the unexpected quasi-independence on the grain size of the open-circuit voltage of these pc-Si solar cells is due to the presence of numerous electrically active intragrain defects.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.