Abstract
A series of SnBi alloys with Bi concentration ranging from 3% to 70% have been studied by nanoindentation technique at room temperature. Constant strain rate (CSR) method was used to evaluate the elastic modulus, hardness and the creep stress exponent of the alloys. SnBi solid solutions with Bi concentration up to 10wt% show significantly higher modulus and hardness than pure Sn. Small amount of Bi precipitates inside Sn-rich phase effectively enhance the hardness and creep resistance of the alloy; while such distribution of Bi particles has no effect on the elastic response of the matrix. The strain rate–stress relationship of the SnBi alloys has been evaluated in the range from 90 to 450MPa. Three stress regions dominated by different rate-controlling mechanisms exist for the SnBi alloys with Bi concentration greater than 10%. At the high stress region (>370MPa), dislocation glide dominates the creep rate where the stress exponents are greater than 10. At the intermediate stress region (200–370MPa), dislocation climb is the dominant creep mechanism with stress exponents around 5–8. When fine lamellar structure is the dominant constituent of the microstructure, phase boundary sliding is identified as the rate-controlling mechanism in the low stress region (<200MPa).
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.