Abstract
Zeolite Beta nanospheres and hollow-boxes are successfully obtained through a simple one-pot hydrothermal crystallization route, using tetraethylammonium hydroxide (TEAOH) as the structure-directing agent (SDA) assisted with a temperature-sensitive bifunctional additive N-methyl-2-pyrrolidone (NMP). The influences of crystallization temperature, Si/Al ratio, and TEAOH content on the synthesis and physicochemical properties of zeolite Beta as well as the formation of hollow structure are investigated in detail. It reveals that the role of NMP changes from “crystallization promoter” (CP) to “hollow-directing agent” (HDA). And the acceleration effect of NMP decreases upon the crystallization temperature (120–160 °C) due to the decomposition of TEAOH. Meanwhile, high synthesis temperature (≥180 °C), high Si/Al ratio (≥30), and low TEAOH content (TEAOH/SiO2 ≤ 0.2) may lead to the formation of undesired zeolites ZSM-5 and/or ZSM-12. The obtained Beta nanosphere and hollow-box catalysts exhibit excellent catalytic activity in the degradation of low-density polyethylene (LDPE) due to their high external surface area and acid density.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.