Abstract
The synthesis of zeolite beta has been studied using the following templating agents: (i) tetraethylammonium hydroxide (TEA;)(ii) tetraethylammonium bromide–diethanolamine; and (iii) tetraethylammonium hydroxide–tetraethylammonium bromide–triethanolamine. TEA+ ions and TEAOH molecules only have a structure-directing effect. The ratio (Si + Al)/TEA+ in the gel was varied from 2 to 10, the Si/Al ratio from 12 to 1000. The temperature of crystallization was chosen in the range 368–443 K. The samples were characterized using X-ray diffraction, micrographs, chemical analysis, thermal analysis, IR spectroscopy and nitrogen adsorption. Zeolite beta of good crystallinity (micropore volume = 0.28 cm3 g–1) was obtained with Si/Al ratios from 14 to 72. The acid strength and number of acid sites were determined from the calorimetrically measured heat of NH3 sorption and from the TPD of NH3. The initial acid strengths of zeolite beta (up to 185 kJ mol–1) are higher than those of other high-silica zeolites.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call