Abstract
The effects of contents of Zn and Gd elements and their mass ratios on microstructure and mechanical properties of as-cast and as-extruded Mg−8Li alloys were investigated. After extrusion, the precipitates are broken, and fine spherical particles with size about 100 nm are found to disperse in the β-Li. The bi-modal structure consisting of long-strip-like coarse-grain α-Mg and recrystallized fine-grain β-Li is formed. The strength and plasticity of the alloys are greatly improved after extrusion, and the YS and UTS increase with the increase of Zn and Gd contents. The Mg−8Li−8Zn−2Gd alloy exhibits an optimum comprehensive performance with the YS of 274 MPa, UTS of 283 MPa, and EL of 39.9%. The bi-modal structure strengthening consisting of the fine crystal strengthening of β-Li and texture strengthening of α-Mg, and the dispersion strengthening of precipitations are the main strengthening mechanisms.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Transactions of Nonferrous Metals Society of China
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.