Abstract
Pure silicide coatings and Y–Ce modified silicide coatings were prepared on Ti–6Al–4V alloy by pack cementation process. The coating structures as well as their wear behaviours were comparatively studied. The results showed that the pure silicide coating and Y–Ce modified silicide coating prepared at 1080°C for 4 h had similar coating structures, mainly consisting of a TiSi2 outer layer, a TiSi middle layer and a Ti5Si4 inner layer. However, the microhardness of the Y–Ce modified silicide coating was higher than that of the pure silicide coating. The wear tests demonstrated that the mass loss of the pure silicide coating was about two times larger than that of the Y–Ce modified silicide coating, indicating the beneficial effects of Y and Ce on the wear resistance of silicide coating.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.