Abstract
This research presents the modification of the microstructure on the surface of a dual phase steel (DP) using three different treatments: surface mechanical attrition treatment (SMAT), surface mechanical carburizing treatment (SMCT), and surface mechanical composite coating treatment (SMCCT). We used SMAT to refine the grain size under high strain and strain rate conditions and successfully induced a phase transformation to martensite. The introduction of carbon during SMAT resulted in surface mechano-chemical carburizing, which enhanced the martensite transformation. Furthermore, the addition of silicon during the process led to the formation of SiC and Fe3C particles dispersed within the ferrite and martensite matrix, creating a surface nano-composite. Analysis using SEM and XRD revealed that the carbon and silicon-treated steel exhibited 41.4% martensite, 4.4% bainite, and 54.1% ferrite, indicating increased transformation by these elements. As a result, the alterations in the surface microstructure led to changes in the mechanical properties of the DP steel. Initially, the DP steel had Y.S. of 250 MPa and U.T.S. of 350 MPa. After SMAT treatment, its Y.S. and U.T.S. increased to 280 MPa and 380 MPa, respectively. The addition of carbon and silicon further enhanced the Y.S. and U.T.S. to 350 MPa and 450 MPa. A significant change in microhardness is achieved from 150HV0.05 to 255HV0.05 while after SMCT and SMCCT is 275HV0.05. Despite an increase in surface roughness contributing to heighten friction, there was a significant reduction in wear. This phenomenon could be attributed to grain refinement, dislocation structures, and martensite phase transformations associated with surface hardening.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Similar Papers
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.