Abstract
This study investigates the effects of adding waste ground glass and lime on the microstructural properties of amorphous gels transitioning into crystallised zeolites in fly-ash-based geopolymers. Three different mix compositions were synthesised using fly ash, waste ground glass powder and calcium hydroxide. These mixtures were subjected to accelerated aging by thermal curing (at a temperature of 80°C), the treatment lasting for 56 d. Crystalline zeolitic phases were detected by Fourier transform infrared spectroscopy and X-ray diffraction. The results show that the transition from amorphous gels into more ordered structures readily occurred in the compositions employing only waste ground glass or calcium hydroxide, whereas a combination of waste ground glass and calcium hydroxide hindered the transition. Moreover, the topographical images of the compositions indicate a greater degree of roughness in the mixture with a lower degree of transition from the amorphous gels into more ordered structures. It was revealed that crystallisation had no harmful effect on the strength stability of the compositions cured for 28 d at a temperature of 80°C. In fact, the maximum increase in the compressive strength occurred due to the formation of crystalline zeolites in fly-ash-based geopolymers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.