Effects of V and Gd doping on novel positive colossal electroresistance and quantum transport in PbPdO2 thin films with (002) preferred orientation.

Abstract

In this work, PbPd0.9V0.1O2 and PbPd0.9Gd0.1O2 thin films with (002) preferred orientation were prepared using a pulsed laser deposition technique. The temperature dependence of resistivities ρI(T) was investigated under various applied DC currents. Colossal electroresistance (CER) effects were found in PbPd0.9V0.1O2 and PbPd0.9Gd0.1O2. It was found that the positive CER values of PbPd0.9V0.1O2 and PbPd0.9Gd0.1O2 reach 3816% and 154% for I = 1.00 μA at 10 K, respectively. In addition, the ρI(T) cycle curves of PbPd0.9V0.1O2 and PbPd0.9Gd0.1O2 thin films showed a critical temperature similar to that of PbPdO2 (Tc = 260 K). Particularly, charge transfer between O1- and O2- was confirmed by in situ XPS. Additionally, based on first-principles calculations and internal electric field models, the CER and magnetic sources in PbPd0.9V0.1O2 and PbPd0.9Gd0.1O2 can be well explained. Finally, it was found that thin film samples doped with V and G ions exhibit weak localization (WL) and weak anti-localization (WAL) quantum transport properties. Ion doping leads to a transition from WAL to WL. The study results indicate that PbPdO2, one of the few oxide topological insulators, can exhibit novel quantum transport behavior after ion doping.