Abstract
Effects of UIT (Ultrasonic impact treatment) on the microstructure and properties of laser welded 1.5mm 441 ferritic stainless steel sheets were studied. Results indicate that the surface of the butt joint generated an ultrasonically induced strengthening layer after UIT. The average microhardness of the layer was increased by 18.1%. The tensile strength of the specimens was increased. Moreover, UIT can decrease the residual stress of welded specimens, the maximum longitudinal tensile stress in the central area was decreased by 78.4%, and the transverse residual stress was converted into compressive stress. The cupping value was increased from 34.5 mm to 37.0 mm following UIT. In addition, the fracture position was changed from the central weld to the edge weld of the cupping hemisphere. The mechanical properties were increased due to the generation of strengthening layers and the decrease of residual stress by UIT.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call