Abstract
Dynamic torsional tests were conducted using a torsional Kolsky bar for five alloys, one of which was fabricated by double-cycled sintering process, and then the test data were compared via microstructures, mechanical properties, adiabatic shear banding, and fracture mode. The double-sintered tungsten alloy specimen whose tungsten particles were very coarse and irregularly shaped showed cleavage fracture in the central area of the gage section with little shear deformation, whereas shear deformation was concentrated in the central area of the gage section in the other alloys. The deformation and fracture behavior of the double-sintered alloy correlated well with the observation of the impacted penetrator specimen and thein situ fracture test results,i.e., microcrack initiation at coarse tungsten particles and cleavage crack propagation through tungsten particles. These findings suggested that the cleavage fracture mode would be beneficial for the serf-sharpening effect and, thus, the improvement of the penetration performance of the double-sintered tungsten heavy alloy would be expected.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.