Friction plug welding (FPW) experiments were performed on 8-mm-thick 2219-T87 FSW welds to investigate the weld formation, microstructure, hardness distribution, mechanical property, and fracture behaviors of FPW joint. The main findings are as follows: geometric size of supporting plate hole and welding force exert great effect on weld formation and mechanical property. Recrystallized zone (RZ) with varied width is observed on the bonding interface between the plug and base metal due to huge friction heat and deformation. Softening is found near the bonding interface due to the disappearance of cold working and transformation of constituent particles. The ultimate tensile strength (UTS) and elongation of FPW joint can reach 336.3MPa and 8%, respectively. The initial fracture of tensile specimen is prone to locate at the lower part of RZ. The tensile fracture morphology of FPW joint is characterized by dimples.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.