The effects of steel slag (SS) addition on the strength and water resistance of magnesium phosphate cement (MPC) are investigated, and the hydration mechanism is proposed in this paper. With the addition of SS, the strength and water resistance of MPC were significantly enhanced. The compressive strength of MPC with 10 wt% SS (SS 10) cured in air for 60 d reached 56.7 ± 4.2 MPa. Interestingly, the strength loss rate of the sample cured in water for 14 d was only 6.6%. In addition, the microstructure and hydration products of MPC specimens were investigated via X-ray diffraction and scanning electron microscopy. There was a significant amount of unreacted MgO after MPC curing, and the main hydration product was struvite-K. The amount of struvite-K (KMgPO4·6H2O) of MPC with 0 wt% SS decreased after curing in water. However, no significant changes in the amount of hydration products was evident for SS 10, and the compactness was enhanced. This work provides a new approach for the resource utilization of SS.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.