Abstract
AbstractIn order to enhance the grafting efficiency of graft copolymerization of granular cornstarch with acrylic acid (AA) for improving the adhesion and film properties of starch‐g‐poly(acrylic acid) used as sizing agent, the esterification of hydrolyzed starch with acryloyl chloride was applied before graft copolymerization. The influence of three common initiators on the copolymerization were also studied. The initiators included ceric ammonium nitrate [Ce(NH4)2(NO3)6], hydrogen peroxide/ferrous ammonium sulfate [H2O2/FeSO4 · (NH4)2SO4], and potassium persulfate/sodium bisulfite [K2S2O8/NaHSO3]. It was found that acryloylation of starch before the copolymerization was an effective method for substantially enhancing the grafting efficiency and improving the performances such as adhesion‐to‐fibers and mechanical properties of grafted starch film. The acryloylation could increase the efficiency to 67–81% when the degree of substitution (DS) of acryloylated starch ranged from 0.010 to 0.036. The adhesion to polyester and cotton fibers reached their maximum at DS = 0.010 and 0.022, respectively. Strong and tough film was obtained when the DS value was in a range of 0.010–0.022. H2O2/FeSO4 · (NH4)2SO4 redox system was more appropriate for initiating the copolymerization of acryloylated starch with AA.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.