Effects of SPEEK/Cloisite Concentration as Electrospinning Parameter on Proton Exchange Membrane for Direct Methanol Fuel Cell Application

Abstract

In this study, a fine fibers mat were produced from SPEEK/Cloisite solution and the effect of the dope concentration on the fibers morphology was performed.The electrospun fibers were denoted as e-spunCL and fabricated as dense membrane (SP/e-spunCL) by immersing electrospun fibers into half-solidified SPEEK solution The fiber’s mechanical stability study was also conducted. The fibers diameters and morphology were observed by using Scanning Electron Microscopy (SEM).While the mechanical properties of the fibers was observed via tensile strength test. The results showed that as the concentration increased (0.05 wt%, 0.10 wt%, 0.17 wt%, 0.25 wt% and 0.30 wt%), the fibers diameters become larger which varies from 9.257 μm to 495.4 nm. The highest tensile strength among all fibers was recorded from SP/e-SpunCL17 which was found to be 19.96882±1.49458MPa. SP/e-spunCL17 showed the most promising physico chemical properties with the highest water uptake and proton conductivity of 25.87±1.9827 %, 12.12±0.2837 mScm-1 and the lowest methanol permeability with 1.22±0.3748 x10-8 cm2s-1.