Abstract
The present work studied the impact of SO42− ions on the corrosion behaviors of GH3535 weld joint in FLiNaK molten salt. The concentration of SO42− ions in the FLiNaK molten salt was controlled by adjusting the quantity of Na2SO4 added into the salt. Results indicate that the SO42− ions in the FLiNaK salt speed up the corrosion rate remarkably by promoting the dissolution of Cr from the alloy matrix into the salt. With the concentration of SO42− ions in the FLiNaK salt increases from 100 ppm to 1000 ppm, the weight losses and the Cr depletion layer depths of the corroded specimens increase linearly. Even in the case of the heavy corrosion attack caused by the SO42− ions, the corrosion performance is similar between the base zone and fusion zone in the GH3535 weld joint. It is demonstrated that the structural diversity caused by the welding process has little impact on the corrosion performances of GH3535 alloy in FLiNaK molten salt.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.