Abstract
Aim of this research was determination of effects of shielding and backing gas pureness on quality of welded joints produced from austenitic stainless-steel grade X5CrNi18-10 (1.4301) pipes Ø 50.8 x 1.5 mm by orbital TIG welding without use of additional material. In the case of stainless steel, it is of importance not only to prepare shielding of the molten metal pool but as well protection of welded joint root from oxygen, which causes formation of colorful oxide layers. Presence of oxidized layer primarily decreases corrosion resistance of stainless-steel. Performed examination included: chemical composition of welded join material, delta ferrite testing, non-destructive joint testing, visual testing with discoloration assessment from face and root side (acc. to Danish Force Technology Institute report 93.34 and American ASME BPE-2012 norm), radiographic testing, destructive welded joint testing. Metallurgical shielding of the welded joint face was produced with Argon 5.0 pure, with a flow rate of 8 dm3/min. Root of welded joint was at first protected with Argon 5.0 pure, then argon-atmospheric air mixtures were used. Backing gas flow rate was set to achieve a relative pressure of 300 Pa. Quantity of residual oxygen in gas mixture was selected based on Danish Force Technology Institute report 93.34.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.