Abstract
This paper reports on the epitaxial growth of hexagonal boron nitride (hBN) films on sapphire substrates in a cold wall chemical vapor deposition (CVD) system where different sapphire nitridation and hBN growth temperatures were employed. A thin and amorphous nitridated layer was formed at a low temperature (850 °C), which enabled subsequent epitaxial hBN growth at 1350 °C. The influences of the sapphire nitridation temperature and the growth temperature on the film quality were analyzed by x-ray diffraction (XRD) measurements. Higher than optimum nitridation and growth temperatures improve the crystalline quality of the nitridated layer, but does not favor the epitaxial growth of hBN. hBN films grown at the optimum conditions exhibit the c-lattice constant of 6.66 Å from the XRD θ–2θ scan and the characteristic in plane stretching vibration at 1370.5 cm−1 from Raman spectroscopy. X-ray photoelectron spectroscopy analysis confirmed the formation of stoichiometric hBN films with excellent uniformity.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.