Abstract
By comparing the structure, dielectric and electrical conduction properties of sintered Ba(Zr0.15Ti0.85)O3 ceramics (short as BZT15) annealed in air and oxygen atmosphere was conducted to explore the impact of oxygen vacancies (OVs) on them. The dielectric properties of the samples were studied as changing with temperature (260–400K) in the scope of frequency from 100 Hz to 100 kHz. A typical relaxor behavior was observed in BZT15 and the relaxor behavior was enhanced after oxygen annealing treatment, which confirmed that the relaxation process was connected with the OVs inside ceramics. The value of activation energy was calculated to be 1.76 eV, 1.79eV, and 1.85 eV for as-prepared, air and oxygen annealed samples, respectively. Besides, the dielectric relaxor behavior was found to be associated with the conductivity originated from the dipolar conduction and long-distance movement of doubly ionized OVs. More interestingly, compared with other ferroelectric materials, the higher activation energy of BZT15 ceramics revealed a weaker concentration of OVs for such dielectric materials.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.