Abstract
The effects of an addition of 0–2 wt% Nd on thermal stability of 0–3 wt% Ca-containing modified AZ71 magnesium alloys was investigated. The ignition temperature was found to increase from that of AZ71, 574, to 825 °C with the addition of 0.5 wt% Ca and 1 wt% Nd. The ignition temperature was further increased to 1114 °C when 3 wt% Ca was added. The Ca- and Nd-added AZ71 was isothermally maintained at a temperature of 500 °C in air for 12 h. The MgO–CaO–Nd2O3 formed on the surface to improve the thermal stability of the AZ71–xCa–yNd alloys. While both the tensile strength and ductility decreased with the Ca concentration in the alloy, an addition of 1 wt% Nd was found able to alleviate the degradation effects of Ca on the tensile strength and ductility at 170 °C. Both solid solution formation and precipitation strengthening contributed to the increase in toughness. AZ71 containing 0.5–2 wt% Ca and 1 wt% Nd provides the optimum combination of ignition resistance and mechanical properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.