Abstract
An experimental study of the structural and magnetic properties of noncrystalline Gd-Co thin films before and after ion implantation has been carried out. The samples have been obtained by a modified RF cosputtering method in a diode-type apparatus. The energy used in implantation was 40 keV with total fluences of 1*10/sup 16/ and 5*10/sup 16/ Ar atoms cm/sup -2/. Rutherford backscattering spectrometry, X-ray, and EDAX techniques have been used for structural analysis. The magnetic domain structure, local hysteresis loops, and coercive forces on the implanted and unimplanted samples were studied using magnetooptic polar Kerr effect (MO) with a metallographic polarizing microscope. The structural measurements pointed to the Gd-Co films being completely amorphous before and after Ar implantation. The MO measurements showed a decrease of magnetic domain width, a progressive diminution of the local hysteresis loop area and an increase of the absolute value of coercive forces for all samples, with increasing doses.< <ETX xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">></ETX>
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.