Abstract

AbstractYoung's moduli of hydrogenated Zr-Nb alloys were evaluated by using a multiple elastometer in the temperature range from room temperature to 773 K, based on the cantilever characteristic vibration technique. The decreasing rate of Young's modulus against the temperature was independent on the additive amount of Nb. The Young's modulus for the hydrogen solid solution of Zr-Nb alloys decreased and that those for the alloys with partially precipitated hydride slightly changed with increasing hydrogen content in both of Zr-1.0Nb and Zr-2.5Nb. The decreasing rates with hydrogen content of hydrogen solid solution of Zr-Nb alloys were almost same as that of Zr hydrogen solid solution. This result was considered because all specimens largely consisted of α-zirconium in which the solute hydrogen was found to decrease the Young's modulus.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.