Abstract
The effects of heat treatment on the ageing response, hardness properties and the microstructure development of Al-6505 alloy have been investigated. In order to study these effects, the alloy sample was solution treated at 550°C for 30 minutes and then quenched into cold water at room temperature followed by artificially aged at elevated temperature of 100 oC, 185 oC and 300 oC. The ageing response of Al-6505 alloy was monitored using Vickers hardness test. The distribution of the precipitates formed in Al-6505 alloy was monitored by transmission electron microscopy (TEM). The results showed that time to reach peak hardness and peak hardness values decreased as the ageing temperatures increased. It was found that increasing in hardness values of the alloy were due to needle-shaped precipitates formation during ageing treatment. Prolonged ageing time to over-aged condition resulting in increased the size but reduced the number of precipitates; as a result the hardness of Al-6505 alloy was reduced. The effects of heat treatment on the ageing response, hardness properties and the microstructure development of Al-6505 alloy have been investigated. In order to study these effects, the alloy sample was solution treated at 550°C for 30 minutes and then quenched into cold water at room temperature followed by artificially aged at elevated temperature of 100 oC, 185 oC and 300 oC. The ageing response of Al-6505 alloy was monitored using Vickers hardness test. The distribution of the precipitates formed in Al-6505 alloy was monitored by transmission electron microscopy (TEM). The results showed that time to reach peak hardness and peak hardness values decreased as the ageing temperatures increased. It was found that increasing in hardness values of the alloy were due to needle-shaped precipitates formation during ageing treatment. Prolonged ageing time to over-aged condition resulting in increased the size but reduced the number of precipitates; as a result the hardness of Al-6505 alloy was reduced.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Uluslararası Muhendislik Arastirma ve Gelistirme Dergisi
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.