Abstract
This paper describes a study on the effects of heat treatment on the microstructure, hardness and wear of aluminum alloys 332 (AlSi9Cu3Mg). The solution treatment was performed at 500°C for 5 hours and then quenched in water at room temperature. Aging was performed at 170°C for 2 hours. The findings revealed that after a full heat treatment, the structure of the eutectic silicon formed toward fragmentation and spheroidization, and the silicon particles became coarse (look-like rounded). Hard intermetallic compound (Mg2Si) appeared on the microstructure after the aging treatment completed. Compared to the as-cast, the hardness of the alloys has improved to 44.84%, and the wear rate of the solution treatment had decreased to 26% while the aging treatment showed a deterioration of 79.42%. The study concludes that aging treatment improves the hardness of AA332 alloys and enhanced the wear resistance of the substance.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call