Abstract
In the present work, the effects of heat treatment and strain rate on mechanical behaviour and microstructure evolution of aluminium alloy 6061 have been investigated. The micro-crack initiation and crystallographic texture evolution are obtained from scanning electron microscope and electron back-scatter diffraction experiments. Quasi-static and high strain rate compression tests are conducted on AA6061 specimens that underwent two different heat treatments: the as-received material with the original T6 heat treatment and the heat treated and artificially aged specimens. For the high strain rate compression (∼2000 and ∼4000 s−1) tests, the split Hopkinson pressure bar apparatus is used. It is observed that the additional heat treatment has significantly reduced the yield strength of the material. Furthermore, electron back-scatter diffraction results show that the higher the applied strain rate is, the less significant change will happen to the texture. Scanning electron microscope images show that, for both T6 and HT specimens, the number and size of micro-cracks in the dynamic compressed specimens are smaller than in the quasi-static deformed specimen. Therefore, the strain rate is considered to be the dominant factor in forming micro-cracks.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.