Abstract

In the present research, an Al7150 alloys-based hybrid nanocomposite was fabricated by incorporating boron carbide and graphene nanoparticles through a novel fabrication method of double ultrasonic two-stage stir casting. Initially, the Al-B4C nanocomposite was optimized based on better microstructural and mechanical properties, and then a hybrid nanocomposite was prepared by incorporating graphene nanoparticles into the optimized Al-B4C nanocomposite. Homogeneous dispersion of graphene and boron carbide nanoparticles in Al7150 matrix was successfully achieved due to the double ultrasonic effect analyzed by Field Emission Scanning Electron Microscopy (FESEM) and High Resolution Transmission Electron Microscopy (HRTEM) analysis. Significant dispersion of nanoreinforcements with enhanced interfacial bonding and dislocation strengthening improved the microstructural and mechanical properties of the Orovan reinforced hybrid nanocomposite. The Vickers microhardness and ultimate tensile strength were improved by 19 % and 47 %, respectively, for the optimized Al-B4C nanocomposite compared to base metal. However, the Vickers microhardness and ultimate tensile strength were significantly improved by 36 % and 57 %, respectively, for the optimized hybrid nanocomposite compared to the base material (BM). The hard AlB2, Al3BC and Al4C3 phases are formed due to the reaction between the matrix and reinforcement during solidification and act as reinforcement within the matrix and resist dislocation movements, resulting in a significant improvement in the mechanical properties of the nanocomposite. Fractography analysis by SEM also confirms the enhanced bonding of graphene nanoparticles as it deforms/slips during fracture and supports the effect of double ultrasonication on the tearing of boron carbide nanoparticles.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.