Effects of friction layer characteristics on the tribological properties of Ni3Al solid-lubricating composites at different load conditions

Abstract

This paper investigates the effects of friction layer characteristics of Ni3Al matrix self-lubricating composites (NMCs) on the tribological properties sliding against ceramic ball Si3N4 at dry friction process at the different load conditions. The characteristics of friction layer are performed in terms of hardness of wear scars, thickness and elemental distributions of friction layer. The results show that the microhardness of wear scars of NMCs increases with the increase of the sliding time and applied load, which results in friction coefficient reduced and wear rate decreased, indicating that the tribological performance of NMCs is obviously affected by microhardness of wear scar. However, under excessive applied load, the performance of friction layer of NMCs is deteriorated for the spalling of wear debris and deformation of contact surface. Therefore, selecting appropriate load conditions during the sliding contact, at the transition to the optimal properties of friction layer maybe occur. NMCs exhibits excellent tribological properties at 15N, which leads to the lowest friction coefficient (0.386) and wear rate (2.48 × 10−5 mm3 N−1 m−1), as well as the smoothest surface of wear track compared with the other load conditions. Meanwhile, the elemental distributions analysis of cross-section of friction layer of NMCs shows that the frictional structures can be divided into three main layers. The thickness of the friction-affected layer varies with the changing of applied load. These results could provide a reference for preparing the solid-lubrication materials with better tribological properties.