Effects of extraction process on the dried cell wall pore structure of messmate heartwood

Abstract

In order to study the effects of a messmate heartwood extraction process on its cell wall pore structure and its drying ability, its nanopore structure was explored after via gas adsorption technology. Specifically, the messmate heartwood particles were extracted with methanol, and then the cell wall pore structure of the original and extracted samples were evaluated by N2 and CO2 sorption and pycnometer methods, respectively. Overall, compared with the original samples, the cell wall porosity, micropore volume, mesopore volume, BET specific surface area, and specific surface area of the micropores of the extracted messmate heartwoods increased by 2.55%, 0.007 cm3/g, 0.0014 cm3/g, 0.24 m2·g-1, and 21.9 m2·g-1, respectively. The cell wall pore volume measured via the gas adsorption method was smaller than the measurement from the pycnometer method. The results indicated that the presence of extractives made the messmate cell wall have a decreased pore volume and porosity, which may be one of the reasons messmate wood is difficult to dry. Messmate extractives primarily were present in the micropores of the cell wall in the range of 0.4 nm to 0.7 nm. However, gas sorption technology could not detect all the pores in the cell wall of the messmate heartwood sample.