Abstract
In this study, the effects of electromigration (EM) on the growth of Cu–Sn intermetallic compounds (IMCs) in Cu/SnBi/Cu solder joints under 5 × 103 A/cm2 direct current stressing at 308, 328, and 348 K were investigated. For each Cu/SnBi/Cu solder joint under current stressing, the IMCs at the cathode side grew faster than that at the anode side. The growth of these IMCs at the anode side and the cathode side were enhanced by electric current. The growth of these IMCs at the cathode followed a parabolic growth law. The kinetics parameters of the growth of the IMCs were calculated from the thickness data of the IMCs at the cathode side at different ambient temperatures. The calculated intrinsic diffusivity (D0) of the Cu–Sn IMCs was 9.91 × 10−5 m2/s, and the activation energy of the growth of the total Cu–Sn IMC layer was 89.2 kJ/mol (0.92 eV).
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.