Abstract
In this study, closure corrected in-phase (IP) and out-of-phase (OP) thermomechanical fatigue crack growth rates at two temperature intervals viz. 573 K to 723 K (300 °C to 450 °C) and 723 K to 873 K (450 °C to 600 °C) of Timetal 834 near α titanium alloy are presented. It is found that closure mechanisms significantly influence the stage I crack growth behavior. Surface roughness-induced crack closure (RICC) predominantly modifies the crack growth rate of near-threshold region at 573 K to 723 K (300 °C to 450 °C) test conditions. However, oxide-induced crack closure further strengthens RICC at 723 K to 873 K (450 °C to 600 °C) TMF loading. In stage II crack growth behavior, the alloy shows higher crack growth rates at 723 K to 873 K (450 °C to 600 °C) OP-TMF loading which is attributed to the combined effect of cyclic hardening occurring at the crack tip and weakening of interlamellar regions due to oxidation.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call