Abstract
The effect of cooling rate on eutectoid decomposition in a near eutectoid (Ti-5.5 at.% Cu) alloy has been investigated in a systematic manner by coupling scanning electron microscopy, transmission electron microscopy and atom probe tomography studies. Thus, the competition between nucleation and growth of proeutectoid α plates from pre-existing β grain boundaries, and eutectoid decomposition (α + Ti2Cu) via a pearlitic mechanism has been studied as a function of cooling rate, using a Jominy-end quenched sample that was cooled from the high-temperature single β phase. When the alloy was subjected to very fast cooling (160 K/s), proeutectoid α plates, supersaturated in Cu, are formed along with a highly refined lamellar eutectoid product between these α plates. In contrast, intermediate (9 K/s) and slow (2 K/s) cooling results in considerably coarser proeutectoid α plates as well as lamellar eutectoid products. With the decrease in the cooling rate, there was a substantial increase in the volume fraction of the lamellar eutectoid product and the composition of all decomposition products approached their equilibrium values. Also, the slowest cooled sample (2 K/s) exhibited substantially rougher and irregular interfaces between the proeutectoid α and the lamellar eutectoid product, which seems to promote the cooperative growth of lamellar α + Ti2Cu. Irrespective of the cooling rate, nucleation of the lamellar eutectoid (α + Ti2Cu) product appears to only occur at the interface between the proeutectoid α plates and the β matrix.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.