Abstract
Effects of Bi nonstoichiometry on (Bi0.5+xNa)TiO3 (BNT) ceramics were investigated at x=−1–+2 mol % of Bi0.5 covering Bi deficiency and excess. At all compositions, rhombohedrally symmetric BNT perovskite formed without secondary phases. Increasing x caused smaller grains. Higher piezoelectric coefficient (d33) but lower depolarization temperature (Td) occurred at Bi excess than at Bi deficiency and vice versa. Leakage current at room temperature decreased with decreasing x. Electrical conductivity of the stoichiometric BNT (x=0) from 700 to 900 °C increased with decreasing partial oxygen pressure from 1 to 10−5 atm suggesting n-type conductivity at elevated temperatures.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.