Abstract
The formation of titanium silicides on Si implanted with different BF2+ dosages has been studied by secondary ion mass spectrometry and transmission electron microscopy measurements. The thickness of the silicide layer formed in the temperature ranging from 600 to 800 °C has been investigated as a function of the implanted BF2+ dosage up to 1×1016 cm−2. Annealing at 700 °C results in conversion of the titanium film into predominantly C49 TiSi2, and most of it is transformed into the C54 phase at 800 °C or higher, resulting in a lower sheet resistance (16 μΩ cm). The titanium silicide thickness formed after the rapid thermal annealing (RTA) treatment depends on the implanted BF2+ dosage, caused by the native oxide enhanced by increased damage. Boron is redistributed into the silicide layer up to the solid solubility limit during annealing, leading to an accumulation at the silicide/silicon interface. The lowest contact resistance (with a size of 0.7 μm×0.7 μm) of 35 Ω is obtained at the annealing temperature of 700 °C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.