Abstract
Ni-P alloys are fabricated on the pre-cleaned copper substrate using electroplating method in sulfate bath. The concentration of phosphorous acid and current density were varied to optimize the P contents as well as the physical properties of the alloy. The properties of Ni-P alloy were analyzed using field emission scanning electron microscopy (FESEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The surface hardness of the Ni-P alloy was increased up to 550 Hv as the phosphorous acid (H3PO3) increased upto 0.015 M, however the higher phosphorous contents in the coating developed the cracked on the surface. The surface hardness was increased due the grain refinement.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.