Abstract
NiCo alloys are electroplated in sulfate bath. The concentration of cobalt sulfate and current density were varied to optimize the surface hardness. The properties of NiCo deposits were analyzed using field emission scanning electron microscopy (FESEM), energy dispersive spectroscopy (EDS) and X-ray diffraction (XRD). The surface hardness of the NiCo alloy was increased up to 500 Hv at 24 wt% Co in the deposits due to the grain refinement. The size of grain was reduced to 12 nm. The residual stress of the deposits was varied from tensile to compressive as the saccharin concentration increased. The zero residual stress was achieved at 0.05 g/L saccharin addition.