Abstract
Autogenous shrinkage of alkali-activated slag cement (AASC) paste prepared with different levels of alkali dosage and silicate modulus (Ms) is investigated. The results show that autogenous shrinkage of AASC paste increases at a decreasing rate with alkali dosage, which is attributed to enhanced capillary pore pressure and syneresis of C-A-S-H gels. Autogenous shrinkage of AASC paste with a constant alkali dosage increases as Ms increases from 0.5 to 1.0, followed with a reduction as Ms further increases to 2.0. Increasing Ms initially enhances the capillary pore pressure due to the enhanced reaction degree, and promotes the formation of saturated capillary pores and viscoelasticity, which facilitates the autogenous shrinkage of AASC paste. However, excessive silicate in the activator retards the internal moisture consumption, and subsequently decreases the autogenous shrinkage of AASC paste. Furthermore, increasing Ms can also intensify syneresis of C-A-S-H gels, contributing to the early-age autogenous shrinkage of AASC paste.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.