Abstract
Precipitation hardening stainless steel (PHSS) possesses high strength, impact resistance, and corrosion resistance, making it extensively employed in aerospace, nuclear power equipment, and petrochemical industries. The precipitates and reversed austenite (RA) generated during heat treatment significantly influence the properties of PHSS. This study investigates the impact of aging temperature (480–620 °C) on PH 13-8Mo stainless steel. As the aging temperature increased from 480 °C to 620 °C, the yield strength (YS) and ultimate tensile strength (UTS) initially increased and then decreased, while the impact energy initially decreased and then increased. At an aging temperature of 510 °C, the strength and hardness reach their maximum values, indicating peak aging conditions. The microstructure after aging treatment is lath martensite, RA and NiAl. With increasing aging temperature, the size of NiAl precipitates increases, accompanied by a rise in RA content. The quantitative analysis assessed the contributions of various strengthening mechanisms (precipitation strengthening, solid solution strengthening, grain refinement strengthening, dislocation strengthening, etc.) to YS. Quantitative calculations revealed that the precipitation strengthening effect was most pronounced at an aging temperature of 510 °C.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.