Abstract
This study aimed to assesses the effect of various commercial Na2SiO3 on the compressive strength (CS) of alkaline activated fly ash mortar (AAFM). The three mixture of alkaline activated mortar (AAM) C1, C2 and C3 were prepared from the source material of fly ash and alkaline activator solution (AAS). The initial AAS was comprised of NaOH (10M) and various grade of Na2SiO3. The various grades of Na2SiO3 were characterized by their SiO2/Na2O molar ratio of 2.0, 2.2, and 3.3, respectively. The sample from each mixture was characterized based on the CS and microstructure changes using useful tools of XRD and FTIR analysis. The results obtained indicated that the highest CS achieved among the three mixtures were 48.23MPa of mixture C2 prepared with SiO2/Na2O molar ratio of 2.2. This was mainly due to higher binder formation (N-A-S-H gel type) and a higher rate of reaction of the main source material. This result is in line with XRD and FTIR analysis results finding.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IOP Conference Series: Materials Science and Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.