Abstract
Pure zinc oxide and Sn-doped ZnO thin films were deposited on a pre-heated glass substrate from tin (II) chloride dihydrate (SnCl2.2H2O) and zinc acetate (Zn(CH3COO))2 precursors using spray pyrolysis technique. The doped films were achieved by adding various quantities of (SnCl2. 2H2O) precursor to the solution of zinc acetate in volume percent range of 0–10. Rutherford Backscattering Spectrometry (RBS) was used to characterise the prepared films to determine their thickness and elemental composition. To examine the films' optical characteristics, a UV spectrometer operating at room temperature and covering a wavelength range of 300–1100 nm was employed. The film's thickness and composition show that as the volume of Sn in the thin films increases, so does the film's thickness. With average transmittance values up to 70 %, all the films are quite transparent in the visible region of the electromagnetic spectrum and have a significant UV cut-off at roughly 380 nm. The reflectivity of Sn-doped ZnO films is seen to be independent of the volume of Sn in the films, and the reflectivity of the films diminishes as the wavelength increases. Sn-doped ZnO thin film has an optical band gap of 3.14–3.18 eV. The properties of the thin film produced make it suitable for solar energy collection and improve the efficiency of solar energy system, various optoelectronics devices and sensor.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.